PREPARATION OF GLASS FIBER REINFORCED COMPOSITE TAPE

Abstract

Abstract: The glass fiber reinforced composite tape can be prepared by first treating the glass fiber by coupling reagent and removing water through heating box, then compositing it with HDPE in the mold and finally making it to be a tape under pressure. This article describes how the glass fiber reinforced composite tapes were prepared under different processing conditions. The purpose of testing the mechanical performance of the tape was to find out the optimal process condition. The results showed that the optimal heating temperature was 170℃ and the optimal speed of fiber passing through the heating box was 6m/min.The optimal pressure for the tape formation was 500N and the optimal tension force was 7N.

Key words: fiber glass, composite tape, coupling agents, tensile strength

CLC Number:

TB332

WANG Da-peng, WANG Qing-zhao, CHENG Quan-biao, XIE Zhi-wei. PREPARATION OF GLASS FIBER REINFORCED COMPOSITE TAPE[J]. COMPOSITES SCIENCE AND ENGINEERING, 2015, 0(10): 68-71.

References

[1] 朱晓峰. 溶液浸渍法制备超高分子量聚乙烯纤维增强复合带. 上海:东华大学,2012.
[2] 南建举, 余俊荣, 朱加尖, 等. 水性聚氨酯基对位芳纶纤维增强复合带的制备与性能. 东华大学学报(自然科学版),2011,37(3):299.
[3] 彭祥. 浅析FRP复合材料在土木工程中的实践效果. 四川水泥,2014, 166.
[4] 徐尚村, 王新定. FRP在隧道工程中的应用探讨. 隧道技术研究, 2009, 737-742.
[5] 陈彦北, 孔令俊, 郝红肖, 等. 一种FRP景观桥应用研究. 铁道建筑, 2014, 34-36.
[6] 吴斌峰, 孙清, 李亮, 等. E玻璃纤维增强环氧树脂基复合材料剪切性能. 输配电技术, 2014, 35(11): 79-84.
[7] 叶列平, 冯鹏. FRP在工程结构中的应用与发展. 土木工程学报,2006, 39(3): 24-36.
[8] 孙丽莉. 玻璃纤维增强树脂基复合材料的细观破坏研究. 山东: 山东大学, 2009.
[9] 冯健中, 游长江, 鲁光, 等. 不饱和聚酯/玻璃纤维复合材料的研究. 广州化学, 2006, 31(3): 45-56.
[10] L.J. Broutman. Glass-Resin Joint Strengths and Their Effiect on Failure Mechanisms in Reinforced Plastics. Polymer Eng and Sic, 1966, 7: 263.
[11] J.P. Favre, J.Perrin. Carbon fibers adhesion to organic matrices. Journal of Material Science, 1972, 7: 1113.
[12] Kazuya N, Michihirot T, Atsushi T, et al. Aggregation structure and molecular motion of interface in short glass-fiber reinforced nylon66 composites. Polymer, 2002, 43(14): 4055-4062.
[13] 张士华, 陈光, 崔崇, 等. 偶联剂处理对玻璃纤维/尼龙复合材料力学性能的影响. 复合材料学报, 2006, 23(3): 31-36.
[14] 刘亚兰, 申士杰, 李龙, 等. 偶联剂处理玻璃纤维表面的研究进展. 绝缘材料, 2010, 43(4): 34-39.
[15] 肖长发. 纤维复合材料-纤维、基体、力学性能. 北京: 中国石化出版社, 1995.