MODELING STUDY ON THERMOMECHANICAL PROPERTIES OF WOVEN QUARTZ/PHENOLIC COMPOSITES

Abstract

Abstract: In this paper, 2.5D quartz fiber/phenolic composites were thermally treated at 800 ℃ for different time. The longest thermal treatment time was 20 min. Then the residual mechanical properties were tested. Mouritz-Mathys model was used to calculate the theoretical values after thermal treatment. The results show that the mechanical properties of the composites decrease sharply with the increase of the thermal treatment time. In all tests, the consistency between measurement and theoretical residual mechanical properties was less than 15%. Using this model, the variation of mechanical properties and time after thermal treatment can be obtained quickly.

Key words: mechanical properties, thermal treatment, modelling

CLC Number:

TB332

YANG Tao, DING Jie, LUO Hai-tao, HUANG Zhi-xiong. MODELING STUDY ON THERMOMECHANICAL PROPERTIES OF WOVEN QUARTZ/PHENOLIC COMPOSITES[J]. Fiber Reinforced Plastics/Composites, 2018, 0(11): 64-67.

References

[1] 时圣波. 高硅氧/酚醛复合材料的烧蚀机理及热-力学性能研究[D]. 哈尔滨: 哈尔滨工业大学, 2013.
[2] 谭珏, 郑裕东, 匡松连, 等. 耐烧蚀硅基纤维布增强酚醛树脂复合材料的高温氧化性能与力学性能[J]. 北京科技大学学报, 2012, 34(6): 677-682.
[3] 李林杰. 高硅氧/酚醛复合材料体积烧蚀条件下的热-力-化学多物理场耦合分析[D]. 哈尔滨: 哈尔滨工业大学, 2014.
[4] 梁馨, 罗丽娟, 谭珏, 等. 美国空间探测器热防护材料发展现状及趋势[J]. 材料导报, 2016(S1): 551-557.
[5] 杨振宇, 俸翔, 苏洲, 等. 2.5D编织复合材料细观结构及弹性性能[J]. 宇航材料工艺, 2010, 40(2): 67-71.
[6] 焦亚男, 仇普霞, 纪高宁, 等. 经纬向纤维体积比例对2.5D机织复合材料力学性能的影响[J]. 天津工业大学学报, 2015(3): 1-5.
[7] 孙颖, 王国军, 张典堂, 等. UHMWPE/乙烯基酯2.5D角联锁机织复合材料动态压缩性能实验研究[J]. 材料工程, 2011(4): 38-42.
[8] S Dai, P R Cunningham, S Marshall, et al. Influence of fibre architecture on the tensile, compressive and flexural behaviour of 3D woven composites[J]. Composites Part A, 2015, 69: 195-207.
[9] 卢子兴, 周原, 冯志海, 等. 2.5D机织复合材料压缩性能实验与数值模拟[J]. 复合材料学报, 2015, 32(1): 150-159.
[10] 纤维增强塑料密度和相对密度试验方法: GB/T 1463—2005[S].
[11] 纤维增强塑料拉伸性能试验方法: GB/T 1447—2005[S].
[12] 纤维增强塑料弯曲性能试验方法: GB/T 1449—2005[S].
[13] Mouritz A P, Mathys Z, Gardiner C P. Thermomechanical modelling the fire properties of fibre-polymer composites[J]. Composites Part B Engineering, 2004, 35(6): 467-474.
[14] Mouritz A P, Mathys Z. Post-fire mechanical properties of marine polymer composites[J]. Composite Structures, 1999, 47(1-4): 643-653.
[15] Mouritz A P, Mathys Z. Post-fire mechanical properties of glass-re-inforced polyester composites[J]. Composites Science & Technology, 2001, 61(4): 475-490.