THE APPLICATION OF RICE BRAN IN GLASS FIBER SIZING

Abstract

Abstract: It is shown by experiment result that the leaching solution of rice bran by water has the potential to be applied in glass fiber sizing agent as film former. After gelatinization and filtration, the film forming ability on glass surface and the sizing ability on glass fiber of the rice bran leaching solution and the solution of imported starch film former were comparatively studied. The leaching solution with surface tension of 38.70mN/m was considered to be a good film former, which could produce glass fiber yarn with high breaking strength (i.e. 4156 cN for 68 tex).

Key words: rice bran, sizing, film-forming agent, glass fiber

CLC Number:

TB332

LV De-hui, LEI Hong, HUO Ji-chuan, GUO Jiong. THE APPLICATION OF RICE BRAN IN GLASS FIBER SIZING[J]. COMPOSITES SCIENCE AND ENGINEERING, 2014, 0(1): 68-71.

References

[1] Loewenstein K.L. Glass science and technology 6, The manufacturing technology of continuous glass fibres[M]. Amsterdam: Elsevier, 1973.
[2] 姜肇中. 我国玻璃纤维工业近期发展概况[J]. 玻璃钢/复合材料,2012,(1): 102-106.
[3] Yu. I. Kolesov, M. Yu. Kudryavtsev, N. Yu. Mikhailenko. Types and Compositions of Glass for Production of Continuous Glass Fiber[J]. 2001, 58: 5-6.
[4] 魏练平,蒋立科,王春艳等. 米糠植酸钙精制工艺及其残渣的利用研究[J].中国粮油学报, 2011, 26(2): 92-98.
[5] Cheryan M. Phytic acid interactions in food systems[J]. Crit Rev Food Sci Nutr, 1980, 13: 297-335.
[6] 王拥政. 水稻副产品米糠的开发前景广阔[J].农村实用科技信息, 2004,(7): 37.
[7] 夏利英,雷洪,霍冀川等. 玻纤浸润用羟丙基玉米淀粉的制备[J]. 精细化工:淀粉化学品,2012, 29(11):1-4.
[8] 程梅,霍冀川,雷洪,李军. 三种进口淀粉用于玻纤浸润剂的研究及其对玻纤性能的影响[J]. 玻璃钢/复合材料,2011,(6): 47-50.
[9] 包昌年, 王鲁宁, 臧树良等. 由米糠提取植酸钙的新方法[P]. 中国: CN1167768A,1997-12-17.
[10] SAULNIER L, MAROT C, ELGORRIAGA M, et al. Thermal and enzymatic treatments for the release of free ferulic from maize bran[J]. Carbohydrate Polymers, 2001, 45: 269-275.
[11] 陈松,赵健,宋绍玲.高氯酸法测定纺织品中淀粉含量[J]. 印染,2006,32(5):40-42.
[12] 周彪,李楠. 含淀粉陶瓷浆料流变性质的研究[J].中国陶瓷,2010, 46(9): 45-48.
[13] Antonucci V, Giordano M, Nicolais L. Resin Flow Monitoring in Resin Film Infusion Process[J]. Materials Processing Technology,2003,(1):687-692.
[14] 王安东,陈阳,李嘉生. 改性环氧基复合材料工艺性能试验研究[J]. 玻璃钢/复合材料,2012,(7): 117-120.
[15] J.L. Willett, F.C. Felker[J]. Polymer, 2005, (46): 3035-3042.
[16] 施美英,薛志云. 纤维临界表面张力测试技术[J].上海化工, 2000, 2(4): 5-7.