Fiber Reinforced Plastics/Composites ›› 2009, Vol. 209 ›› Issue (1): 28-30.
• MATERIAL RESEARCH • Previous Articles Next Articles
Online:
Published:
Abstract:
In this paper, the epoxy resin system was prepared by applying liquid amine to the modified epoxy resin,which was the mixture of CYD128 and epoxy A. The results showed that the viscosity of the resin system was 255cps at 30℃. It was the moderate temperature curing epoxy resin system. And the tensile strength, tensile module, flexural strength, flexural module of the cured resin product were 67.7 MPa, 3.1GPa, 101MPa and 2.87GPa respectively. The system can meet the requirement of RTM.
CLC Number:
TQ323.5
CHAI Hong-Mei, WANG Lei, LV Jin-Yan. STUDY ON THE MODERATE TEMPERATURE CURING EPOXY RESIN SYSTEM FOR RESIN TRANSFER MOLDING[J]. Fiber Reinforced Plastics/Composites, 2009, 209(1): 28-30.
/ Recommend
Add to citation manager EndNote|Ris|BibTeX
URL: https://frp.cn/EN/
https://frp.cn/EN/Y2009/V209/I1/28
［1］ 马青松，陈朝辉，郑文伟等.树脂传递模塑复合材料成型新工艺［J］.材料科学与工程，2000,18(4):9497. ［2］ 李萍等.RTM技术的发展及在航空工业中的应用［J］ .材料工程，1998,(1):46. ［3］ 包建文，陈祥宝等.长期贮存单组分RTM环氧树脂研究［J］.热固性树脂，2001,16（5):1820. ［4］ 尹昌平,刘钧,曾竟成, RTM工艺用双酚F型环氧树脂体系研究［J］. 玻璃钢/复合材料,2006,（27):2631. ［5］ 邓杰.高性能复合材料树脂传递膜技术(RTM)研究［J］. 纤维复合材料,2005,（01）:5053. ［6］ 乌云其其格.3233树脂及其碳布复合材料的性能研究［J］.纤维复合材料，2004,（04）:68. ［7］ 梁志勇，段跃新，林云等.RTM专用混合型树脂体系研究反应特性与工艺特征研究［J］.玻璃钢/复合材料,2000,(05): 1417. ［8］ 尹昌平,刘钧,曾竟成.RTM 工艺用双酚F型环氧树脂体系研究［J］. 玻璃钢/复合材料，2006，(02):2731.