STUDY ON THE HOT DIAPHRAGM FORMING OF CARBON FIBER COMPOSITE WITH BEAM AND RIB PARTS

Abstract

Abstract: The 3234/T700 carbon fiber composite beam/rib parts was prepared by a home-made hot diaphragm forming equipment, and cured into the autoclave. The effect of forming temperature, forming time and thickness on the forming process was investigated by the surface quality, mechanical properties, thickness and internal defects of the cured parts. The result shows that the quality of the parts can be improved by increasing the forming temperature and forming time appropriately.

Key words: thermosetting composite, hot diaphragm forming, beam/rib parts, prepreg

CLC Number:

TB332

WANG Dong-dong, XU Heng-yuan, GONG Zhi-hong, LI Cheng-long. STUDY ON THE HOT DIAPHRAGM FORMING OF CARBON FIBER COMPOSITE WITH BEAM AND RIB PARTS[J]. Fiber Reinforced Plastics/Composites, 2016, 0(10): 50-55.

References

[1] 吴志恩. 复合材料热隔膜成型[J]. 航空制造技术, 2009(25):113-116.
[2] 匡载平, 戴棣, 王雪明. 热隔膜成型技术[C]//复合材料: 创新与可持续发展. 2010.
[3] 陈亚莉. 复合材料成型工艺在A400M军用运输机上的应用[J]. 航空制造技术, 2008(10):32-35.
[4] Monaghan M R, Mallon P J. High temperature mechanical characterisation of polyimide diaphragm forming films[J]. Composites Part A: Applied Science & Manufacturing, 1998, 29(3):265-272.
[5] Gutowski T G, Dillon G, Chey S, et al. Laminate wrinkling scaling laws for ideal composites[J]. Composites Manufacturing, 1995, 6(3,4):123-134.
[6] Bersee H E N, Beukers A. Diaphragm forming of continuous fibre reinforced thermoplastics: influence of temperature, pressure and forming velocity on the forming of Upilex-Rw diaphragms[J]. Composites Part A: Applied Science & Manufacturing, 2002, 33(7):949-958.
[7] Delaloye S, Niedermeier M. Optimization of the diaphragm forming process for continuous fibre-reinforced advanced thermoplastic composites[J]. Composites Manufacturing, 1995, 6(3,4):135-144.
[8] Keane M A, Mulhern M B, Mallon P J, et al. Investigation of the effects of varying the processing parameters in diaphragm forming of advanced thermoplastic composite laminates[J]. Composites Manufacturing, 1995, 6(3,4):145-152.
[9] Krebs J, Friedrich K, Bhattacharyya D. A direct comparison of matched-die versus diaphragm forming[J]. Composites Part A: Applied Science & Manufacturing, 1998, 29(1):183-188.
[10] Mallon P J, O'Brádaigh C M, Pipes R B. Polymeric diaphragm forming of complex-curvature thermoplastic composites[J]. Composites, 1989, 20(1):48-56.
[11] Pantelakis S G, Baxevani E A. Optimization of the diaphragm forming process with regard to product quality and cost[J]. Composites Part A: Applied Science & Manufacturing, 2002, 33(4):459-470.
[12] 边旭霞, 顾轶卓, 孙晶, 等. 热隔膜工艺温度与成型速率对C形复合材料成型质量的影响[J]. 玻璃钢/复合材料, 2013(5).
[13] 姚双, 李敏, 顾轶卓, 等. 碳纤维复合材料C形结构热隔膜成型工艺[J]. 北京航空航天大学学报, 2013, 39(1):95-99.
[14] Ersoy N, Potter K, Wisnom M R, et al. An experimental method to study the frictional processes during composites manufacturing[J]. Composites Part A:Applied Science & Manufacturing, 2005, 36(11):1536-1544.
[15] Martin C J, Seferis J C, Wilhelm M A. Frictional resistance of ther-moset prepregs and its influence on honeycomb composite processing[J]. Composites Part A: Applied Science & Manufacturing, 1996, 27(10):943-951.
[16] Maulik D, Karantza M, Spandou E, et al. On the Effect of Temperature on the Creep Behavior of Neat and Carbon Fiber Reinforced PEEK and Epoxy Resin[J]. Journal of Composite Materials, 1995, 29(3):372-387.