VOLUME POROSITY MEASUREMENT OF CFRP BASED ON MICRO-CT TECHNOLOGY

Abstract

Abstract: A new method was proposed for volume porosity measurement based on micro-CT technology. The principle of micro-CT technology was analyzed, picture processing of results was done, and volume porosity was quantitated. The results show that micro-CT technology can be effectivly used on CFRP volume porosity measurement, and matrix and voids distinguish. In order to obtain accurate porosity result, large volume of representative specimen is necessary.

Key words: micro-CT technology, CFRP, volume porosity

CLC Number:

TB332

XIAO Peng, LIU Kui. VOLUME POROSITY MEASUREMENT OF CFRP BASED ON MICRO-CT TECHNOLOGY[J]. Fiber Reinforced Plastics/Composites, 2018, 0(1): 94-97.

References

[1] 周正干, 黄凤英, 魏东. 复合材料孔隙率超声检测方法综述[J]. 航空制造技术, 2009(15): 104-106.
[2] 张立功, 张佐光. 先进复合材料中主要缺陷分析[J]. 玻璃钢/复合材料, 2001(2): 42-45.
[3] 张阿樱,张东兴,朱洪艳, 等. 碳纤维/环氧树脂层压板孔隙率及力学性能的试验表征[J]. 玻璃钢/复合材料, 2011(1): 24-28.
[4] 碳纤维增强塑料孔隙含量和纤维体积含量试验方法: GB/T 3365—2008[S]. 2008.
[5] 肖鹏, 刘卫平, 刘奎, 等. 碳纤维复合材料孔隙分布及形貌分析研究[J]. 玻璃钢/复合材料, 2016(6): 62-66.
[6] 刘玲, 张博明, 王殿富. 碳/环氧复合材料孔隙问题研究进展[J]. 宇航材料工艺, 2004(6): 6-10.
[7] 曹玉玲, 孙玲霞. 工业CT在复合材料孔隙率分析中的应用[J]. CT理论与应用研究, 2001(4): 14-17.
[8] 吴问全, 李伟, 李文杰, 等.基于Nano-CT技术研究多孔陶瓷材料的三维结构[J]. 核技术, 2010, 33(4): 241-245.
[9] 江柏红, 周金帅, 高晓进, 等. 基于显微CT技术的C/C-SiC复合材料孔隙率测量方法[J]. 宇航材料工艺, 2015(4): 122-126.
[10] 冯炎建, 冯祖德, 李思维, 等. C/SiC表面SiC涂层氧化的显微CT无损检测与分析[J]. 复合材料学报, 2011, 28(5): 126-132.
[11] 敖波, 张小海, 李春阳, 等. 疲劳裂纹扩展高分辨率CT 分析新进展[J]. CT 理论与应用研究, 2010, 19(2) : 35-41.
[12] 吴东流. 复合材料CT检测的原理和应用[J]. 宇航材料工艺, 2001(1): 42-48.
[13] 汪赫男, 张佐光, 顾轶卓, 等. 环氧复合材料层板热压成型孔隙缺陷影响因素[J]. 复合材料学报, 2007(5): 55-60.
[14] 陈超, 张娅婷, 顾轶卓, 等. 碳纤维/环氧复合材料孔隙缺陷的工艺影响因素研究[J]. 玻璃钢/复合材料, 2014(5): 51-55.
[15] 徐骥威, 李敏, 顾轶卓, 等. 热固性树脂中孔隙形成条件的定量测试方法与影响因素[J]. 复合材料学报, 2008(2) : 52-56.