STUDY ON THE FIBER DISTRIBUTION OF EPOXY SHEET MOLDING COMPOUND IN THE PROCESS OF COMPRESSION MOLDING

Fiber Reinforced Plastics/Composites ›› 2017, Vol. 0 ›› Issue (2): 54-59.

• APPLICATION RESEARCH • Previous Articles Next Articles

STUDY ON THE FIBER DISTRIBUTION OF EPOXY SHEET MOLDING COMPOUND IN THE PROCESS OF COMPRESSION MOLDING

XU Jiao-jiao¹ , LI Jian^1*, HUANG Zhi-xiong²

1.School of Materials Science and Engineering, Hubei University of Automotive Technology, Shiyan 442002, China;
2.School of Materials Science and Engineering, Wuhan University of Technology, Wuhan 430070, China

Received:2016-08-14 Online:2017-02-28 Published:2017-02-28

Abstract

Abstract: The fiber flowing and distribution of epoxy sheet molding compound(ESMC) have great effect on the properties of ESMC parts. In this article, the relationships between raw materials, viscosity of ESMC sheets, molding parameters etc. and fiber distribution were systematically studied by measuring the fiber content of ESMC parts. The results showed that when the fiber content of ESMC was 24%, the length of fibers was 24 mm, the size of filler was 45 μm, the viscosity of ESMC sheets was 5 × 10³ Pa·s, the layering area was 60% and the velocity of mould closing was 1 mm/s, indicating a better fiber distribution of ESMC parts.

Key words: epoxy sheet molding compound, fiber distribution, mold flowing

CLC Number:

TB332

XU Jiao-jiao , LI Jian, HUANG Zhi-xiong. STUDY ON THE FIBER DISTRIBUTION OF EPOXY SHEET MOLDING COMPOUND IN THE PROCESS OF COMPRESSION MOLDING[J]. Fiber Reinforced Plastics/Composites, 2017, 0(2): 54-59.

References

[1] 陈平, 王德中. 环氧树脂及其应用[M]. 北京:化学工业出版社, 2004.
[2] 黄家康. 复合材料成型技术及应用[M]. 北京:化学工业出版社, 2011.
[3] 柴红梅, 代海涛, 丁勇钢. 环氧树脂团状模塑料制备及其性能研究[J]. 玻璃钢/复合材料, 2014 (5): 56-58.
[4] 吴雪平, 代建建, 汤瑛召,等. 模压成型环氧树脂/玄武岩纤维复合材料研究[J]. 工程塑料应用, 2016, 44(1): 16-21.
[5] Daisuke Shimamoto, Yuichi Tominaga, Yusuke IMAI, et al . Fiber orientation and flexural properties of short carbon fiber/epoxy composites[J]. Journal of the Ceramic Society of Japan, 2016, 124 (1): 125-128.
[6] 黄志雄, 张凯, 于浩, 等. 低压片状模塑料纤维分布与模内粘度控制[J]. 武汉理工大学学报, 2007, 29(4): 11-13.
[7] Francisco J Hurtado, Antonio S Kaiser, Antonio Viedma, et al. Numerical study of the vacuum infusion process for laminated composites with different fiber orientations[J]. Journal of Reinforced Plastics and Composites, 2015, 34(3): 196-212.
[8] 黄家康. 我国玻璃钢模压成型工艺的发展回顾及现状[J]. 玻璃钢/复合材料, 2014 (9): 24-33.
[9] Mahmood M Shokrieh, Reza Mosalmani. Modeling of sheet molding compound compression molding under non-isothermal conditions[J]. Journal of Reinforced Plastics and Composites, 2014, 33(13): 1183-1198.
[10] B.J. Yang, B.R. Kim, H.K. Lee. Predictions of viscoelastic strain rate dependent behavior of fiber-reinforced polymeric composites[J]. Composite Structures, 2012, 94(4): 1420-1429.
[11] 蔡浩鹏, 王钧, 黄绪棚. 玻璃纤维毡增强聚丙烯在冲压成型中的纤维分布研究[J]. 玻璃钢/复合材料, 2004 (5): 42-44.
[12] 程燕婷, 孟家光, 刘青, 等. 碳纤维-环氧树脂复合材料的制备及力学性能表征[J].合成纤维, 2016, 45(3): 38-42.
[13] D.G. Yang, K.M.B. Jansen, L.J. Ernst, et al. Effect of filler concentration of rubbery shear and bulk modulus of molding compounds[J]. Microelectronics Reliability, 2007, 47 (2-3): 233-239.
[14] 沈苏华, 林建忠. 纤维悬浮槽道湍流中纤维取向分布和流变特性[J]. 浙江大学学报(工学版), 2006, 40 (12): 2093-2097.
[15] 杨进军. 纤维分布对复合材料固化变形的影响[J]. 纤维复合材料, 2010 (1): 13-17.
[16] Lisa M., Abrams M.S. Processing studies in sheet molding compound compression molding[D]. Columbus: Philosophy in the Graduate School of the Ohio State University, 2001.

STUDY ON THE FIBER DISTRIBUTION OF EPOXY SHEET MOLDING COMPOUND IN THE PROCESS OF COMPRESSION MOLDING

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 2

Recommended Articles

Metrics

Comments

[1]	HUANG Zhen-yuan, CHENG Bin, ZHAO Ya-meng, CHEN Yi. FINE CHARACTERIZATION OF THE FIBER DISTRIBUTION OF SHORT CARBON FIBER REINFORCED PLASTIC [J]. Composites Science and Engineering, 2020, 0(3): 26-30.
[2]	ZHU Han-rui, GU Yi-zhuo, MENG Qing-yu, ZHANG Zuo-guang. STUDY ON FIBER DISTRIBUTION IN INJECTION-MOLDED LGF/PA COMPOSITE WHEEL [J]. Fiber Reinforced Plastics/Composites, 2018, 0(11): 50-57.